| Aluminum Silicate, Extender Slurries (Formulation #21-10006) | Patcham LTD | Gradually add cellulosic thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1. Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing f...voir plus Gradually add cellulosic thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1. Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing for 10 minutes at 2 ms-1. Grind the mill base using Glass beads for 2 hours at 21 ms-1 μm / gauge 7+ NS. voir moins | |
| Calcium Carbonate, Extender Slurries (Formulation #21-10006) | Patcham LTD | Gradually add cellulosic thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1. Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing f...voir plus Gradually add cellulosic thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1. Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing for 10 minutes at 2 ms-1. Grind the mill base using Glass beads for 2 hours at 21 ms-1 μm/ gauge 7+ NS. voir moins | |
| Dispersion-Silicate Facade Paint, Water Based (Formulation #F14402.0 [1]) | Hoffmann Mineral 霍夫曼矿物 | Dispersion-Silicate Facade Paint, Water Based (Formulation #F14402.0 [1]) featuring SILLITIN N 85. | |
| High Gloss White Coat Paint (Formulation #07-1021B) | Ashland | PVC 20% - Synaqua* 4804 alkyd emulsion high gloss white top coat. | |
| High Gloss White Top Coat - Higher Solids (Formulation #07-1022B) | Ashland | PVC 20% - Uradil* AZ 785-Z52 alkyd emulsion high gloss white top coat. | |
| High Gloss White Top Coat (Formulation #07-1023B) | Ashland | PVC 19% - Primal* HG 74D acrylic high gloss white paint. | |
| High Gloss White Top Coat (Formulation #07-1024B) | Ashland | PVC 19% - Primal* HG 74D - acrylic high gloss white top coat. | |
| High Gloss White Top Coat (Formulation #07-1025B) | Ashland | PVC 20% - Uradil* AZ 785-Z52 alkyd emulsion high gloss white top coat. | |
| High Gloss White Top Coat (Formulation #07-1030B) | Ashland | PVC 20 % - Synthalat* PWM 883 alkyd emulsion high gloss white top coat. | |
| High Gloss White Top Coat (Formulation #07-1075A) | Ashland | This PVC 20% - NeoPac PU 580 urethane alkyd emulsion high gloss white top coat features Aquaflow™ NHS-350E. | |
| High Quality Facade Paint, Solvent-based (Formulation #F20102.0 [1]) | Hoffmann Mineral 霍夫曼矿物 | High Quality Facade Paint, Solvent-based (Formulation #F20102.0 [1]) featuring SILLITIN Z 89. | |
| Interior / Exterior Deeptone Semi Gloss Paint (Formulation #07-1018B) | Ashland | PVC 43% - Acronal* S559 styrene acrylic deeptone semi-gloss paint. | |
| Interior / Exterior Semi Gloss Paint (Formulation #07-1031B) | Ashland | PVC 30% - Neocryl* XK-90 acrylic semi-gloss white paint. | |
| Interior / Exterior Semi Matt Paint (Formulation #07-1034A) | Ashland | PVC 38% - Acronal* S 559 styrene acrylic interior semi matt white paint featuring Natrosol™ HE 3KB hydrophobically modified hydroxyethylcellulose (HMHEC) & Aquaflow™ NMS-450 rheology modifier. | |
| Interior / Exterior Semi Matt Paint (Formulation #07-1035A) | Ashland | PVC 38% - Mowilith* LDM 1871 vinyl acetate ethylene interior semi matt white paint featuring Natrosol™ HE 3KB hydrophobically modified hydroxyethylcellulose (HMHEC). | |
| Interior / Exterior Semi-Gloss Paint (Formulation #07-1032B) | Ashland | PVC 30% - Neocryl* XK-90 acrylic semi-gloss white paint. | |
| Interior / Exterior Semi-Matt Paint (Formulation #07-1033B) | Ashland | PVC 38% - Mowilith* LDM 1871 vinyl acetate ethylene interior semi-matt white paint. | |
| Interior / Exterior Semi-Matt Paint (Formulation #07-1036B) | Ashland | PVC 38% - Alberdingk* AS 6002 styrene acrylic interior semi-matt white paint. | |
| Interior / Exterior Semi-Matt Paint (Formulation #07-1037B) | Ashland | PVC 38% - Vinnapas* EZ 3010 vinyl acetate ethylene interior semi-matt white paint. | |
| Interior/Exterior Gloss Paint (Formulation #21-10005) | Patcham LTD | Gradually add Cellulosic Thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing ...voir plus Gradually add Cellulosic Thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing for 10 minutes at 2 ms-1. Grind at 4 ms-1 until desired Hegman gauge is achieved- 7+ NS/ <10 μm. voir moins | |
| Interior/Exterior Matt Paint (Formulation #21-10005) | Patcham LTD | Gradually add Cellulosic Thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing ...voir plus Gradually add Cellulosic Thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing for 10 minutes at 2 ms-1. Grind at 4 ms-1 until desired Hegman gauge is achieved. 5+ NS/ min. of 20 μm. voir moins | |
| Interior/Exterior Semi Glossy Paint Waterborne Coatings (Formulation #21-10005) | Patcham LTD | Gradually add Cellulosic Thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing ...voir plus Gradually add Cellulosic Thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing for 10 minutes at 2 ms-1. Grind at 4 ms-1 until desired Hegman gauge is achieved. -7 NS/ min. of 15 μm. voir moins | |
| Interior/Exterior Semi-Matt Paint (Formulation #07-1039B) | Ashland | PVC 38% - Acronal S559* styrene acrylic semi-matt white paint. | |
| Matt Paint 1 (Formulation #SPF_CTG_021_2203) | Arkema Rheology & Specialty Additives | This matt paint features Ecodis™ P 50. | |
| Matt Paint 2 (Formulation #SPF_CTG_022_2203) | Arkema Rheology & Specialty Additives | This matt paint features Ecodis™ P 50. | |
| Matt Paint 3 (Formulation #SPF_CTG_023_2203) | Arkema Rheology & Specialty Additives | This matt paint features Ecodis™ P 50. | |
| Talc, Extender Slurries (Formulation #21-10006) | Patcham LTD | Gradually add cellulosic thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing ...voir plus Gradually add cellulosic thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing 10 minutes at 2 ms-1. Grind the mill base using Glass beads for 2 hours at 21 ms-1 μm / gauge 7+ NS. voir moins | |
| Zinc Oxide, Extender Slurries (Formulation #21-10006) | Patcham LTD | Gradually add cellulosic thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing ...voir plus Gradually add cellulosic thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing 10 minutes at 2 ms-1. Grind the mill base using Glass beads for 2 hours at 21 ms-1 μm / gauge 7+ NS. voir moins |