(PC+ABS)-Blend; Vicat/B 120 temperature = 113°C; for electroplating applications

Rubber modified PC blend; 10 % mineral filled; flame retardant; Vicat/B 120 temperature = 108°C; extrusion grade; good extrusion and vacuum-forming behaviour; UL-recognition 94 V-0 at 0.75mm; glow wire temperature (GWFI): 960°C at 2.0 mm

(PC+ABS)-Blend; flame retardant; high heat resistance; Vicat/B 120 temperature = 136°C; ball indentation temperature >= 125°C; UL recognition 94 V-0 at 1.5 mm; suitable as supporting material for energized parts

(PC+ABS)-Blend; easy flowing; Vicat/B 120 temperature = 103°C; UL recognition 94 V-0 at 1.5 mm; no juicing; good light stability

(PC+ABS)-Blend; flame retardant; Vicat/B 120 temperature = 97°C; compared to FR3000 improved chemical resistance and stress cracking behavior; UL recognition 94 V-0 at 1.5 mm

(PC+ABS)-Blend; flame retardant; easy flowing; Vicat/B 120 temperature = 97°C; UL recognition 94 V-0 at 1.5 mm; Glow wire test: 960°C at 2.0 mm; no juicing; good light stability

(PC+ABS)-Blend; Vicat/B 120 temperature = 103°C; UL recognition 94 V-0 at 1.5 mm; glow wire temperature (GWFI): 960°C at 2.0 mm

(PC+ABS)-Blend; flame retardant; Vicat/B 120 temperature = 99°C; UL recognition 94 V-0 (1.0 mm); glow wire temperature (GWFI): 960°C at 2.0 mm; for notebooks and thinwall applications

(PC+ABS)-Blend; flame retardant; Vicat/B 120 temperature = 89°C; improved chemical resistance; UL recognition 94 V-0 at 1.5 mm

(PC+ABS)-Blend; flame retardant; very easy-flowing; Vicat/B 120 temperature = 96°C; UL recognition 94 V-0 at 1.5 mm; Components for the electrical/electronics sector

(PC+ABS)-Blend; flame retardant; very easy-flowing; Vicat/B 120 temperature = 96°C; UL recognition 94 V-0 at 1.5 mm

(PC+ABS)-Blend; flame retardant; Vicat/B 120 temperature = 108°C; easy flow version of FR3006; increased heat resistance; UL recognition 94 V-1 at 1.5 mm, V-0 at 1.8 mm and 5VB at 1.8 mm

(PC+ABS)-Blend; flame retardant; Vicat/B 120 temperature = 103°C; improved chemical and very good hydrolysis resistance; HDT/A >= 85°C; UL recognition 94 V-0 at 1.5 mm; Glow wire test: 960°C at 2.0 mm; good light stability

(PC+ABS)-Blend; flame retardant; Vicat/B 120 temperature = 103°C; improved chemical and very good hydrolysis resistance; HDT/A >= 85°C; UL recognition 94 V-0 at 1.5 mm; glow wire temperature (GWFI): 960°C at 2.0 mm; good light stability Partially bio-circular grade / Attributed via mass balance (according to ISCC PLUS Standard).

(PC+ABS)-Blend; flame retardant; Vicat/B 120 temperature = 103°C; improved chemical and very good hydrolysis resistance; HDT/A >= 85°C; UL recognition 94 V-0 at 1.5 mm; glow wire temperature (GWFI): 960°C at 2.0 mm; good light stability

(PC+ABS)-Blend; flame retardant; Vicat/B 120 temperature = 103°C; UL recognition 94 5VB at 1.8 mm; successor to FR3000 BBS066; Improved hydrolysis resistance

(PC+ABS)-Blend; flame retardant; easy flowing; Vicat/B 120 temperature = 108°C; UL recognition 94 V-0 at 1.5 mm; glow wire temperature (GWFI): 960°C at 2.0 mm; optimized processability; good light stability

(PC+ABS)-Blend; flame retardant; Vicat/B 120 temperature = 108°C; increased heat resistance; UL recognition 94 5VB (1.5 mm); glow wire temperature (GWFI): 960°C at 2.0 mm

(PC+ABS)-Blend; flame retardant; Vicat/B 120 temperature = 110°C; increased heat resistance; UL recognition 94 V-0 at 1.5 mm; glow wire temperature (GWFI): 960°C at 2.0 mm; improved chemical resistance and stress cracking behavior; successor to FR2010 Partially bio-circular grade / Attributed via mass balance (according to ISCC PLUS Standard).

(PC+ABS)-Blend; flame retardant; Vicat/B 120 temperature = 110°C; increased heat resistance; UL recognition 94 V-0 at 1.5 mm; glow wire temperature (GWFI): 960°C at 2.0 mm; improved chemical resistance and stress cracking behavior; successor to FR2010

(PC+ABS)-Blend; flame retardant; easy flowing; Vicat/B 120 temperature = 118°C; good heat resistance; UL recognition 94 V-0 at 1.5 mm; glow wire temperature (GWFI): 960°C at 2.0 mm; good light stability

(PC+ABS)-Blend; flame retardant; Vicat/B 120 temperature = 102°C; UL recognition 94 V-1 (1.5 mm); good light stability

(PC+ABS)-Blend; flame retardant; impact modified; easy flowing; Vicat/B 120 temperature = 95°C; for: information technology

(PC-I)-Blend; flame retardant; Vicat/B 120 temperature = 101 °C; UL-recognition 94 V-0 at 0.75mm; rated f1 per UL746 C "Outdoor Suitability"; improved colorability compared to other PC+ASA grades

mineral filled PC blend; 5 % mineral filled; UV-stabilized; Vicat/B 120 temperature = 102°C; flame-retardant;; UL recognition 94 V-0 (0.6mm); low smoke density

(PC+ABS)-Blend; 5 % mineral filled; flame retardant; Vicat/B 120 temperature = 103°C; HDT/A >= 85°C; for thin-wall applications; very good UL recognition in small wall thicknesses (V-0 at 0.75 mm); low smoke density

(PC+ABS)-Blend; 15 % mineral filled; with 30 % post consumer recyclate - water bottle content; flame retardant; Vicat/B 120 temperature = 97°C; increased stiffness; tensile modulus = 4600 MPa; UL recognition 94 V-0 at 1.5 mm

(PC+ABS)-Blend; 15 % mineral filled; with 30 % post consumer recyclate; Vicat/B 120 temperature = 98 °C; medium viscosity; medium modulus; low warpage; flame-retardant

(PC+ABS)-Blend; 15 % mineral filled; flame retardant; Vicat/B 120 temperature = 98°C; high stiffness; tensile modulus = 4800 MPa;; UL recognition 94 V-0 at 1.5 mm; glow wire temperature (GWFI): 960°C at 2.0 mm Partially bio-circular grade / Attributed via mass balance (according to ISCC PLUS Standard).

(PC+ABS)-Blend; 15 % mineral filled; flame retardant; Vicat/B 120 temperature = 98°C; high stiffness; tensile modulus = 4800 MPa;; UL recognition 94 V-0 at 1.5 mm; glow wire temperature (GWFI): 960°C at 2.0 mm

(PC+ABS)-Blend; flame retardant; mineral filled ; containing 35% post-consumer PC recyclate; Vicat/B 120 temperature = 102°C; UL recognition 94 V-0 at 1.2 mm; low warpage; improved stiffness and surface quality; for notebooks and thinwall applications Partially bio-circular grade / Attributed via mass balance (according to ISCC PLUS Standard).

(PC+ABS)-Blend; flame retardant; mineral filled ; containing 35% post-consumer PC recyclate; Vicat/B 120 temperature = 102°C; UL recognition 94 V-0 at 1.2 mm; low warpage; improved stiffness and surface quality; for notebooks and thinwall applications

(PC+ABS)-Blend; flame retardant; mineral filled ; Vicat/B 120 temperature = 102°C; UL recognition 94 V-0 at 1.2 mm; low warpage; improved stiffness and surface quality; for notebooks and thinwall applications

(PC+ABS)-Blend; flame retardant; Vicat/B 120 temperature = 115°C; extrusion grade; good extrusion and vacuum-forming behaviour; UL recognition 94 V-0 at 1.5 mm; halogen-free according to DIN VDE 0472,815; glow wire temperature (GWFI): 960°C at 1.0 mm

(PC+ABS)-Blend; flame retardant; low viscocity; non-reinforced; impact modified; Easy flow; Vicat/B 120 temperature = 108 °C; Housing; for: information technology; Electrical/electronic

(PC+ABS)-Blend; flame retardant; good UV/light transmission (e 380 nm) at low wall thicknesses for UV/light curing adhesives; for thin-wall applications; UL recognition 94 V-0 (1.0 mm); only natural color (000000) available; for thin-wall applications

containing 35% post-consumer PC recyclate; flame retardant; injection molding grade; for notebooks and thinwall applications

containing 35% post-consumer PC recyclate; flame retardant; injection molding grade; for notebooks and thinwall applications

PC+ABS-FR(40)-Blend; flame retardant; for notebooks and thinwall applications Partially bio-circular grade / Attributed via mass balance (according to ISCC PLUS Standard).

PC+ABS-FR(40)-Blend; flame retardant; for notebooks and thinwall applications