| DA-310 | DCC (Dairen Chemical Corp.) | DA-310 is a non-plasticized, aqueous, milky, white vinyl acetate-ethylene copolymer emulsion containing incorporated carboxylic groups. It exhibits VAE emulsion properties together with increased adhesion to metals, like aluminum. DA-310 is used for seali...展开 DA-310 is a non-plasticized, aqueous, milky, white vinyl acetate-ethylene copolymer emulsion containing incorporated carboxylic groups. It exhibits VAE emulsion properties together with increased adhesion to metals, like aluminum. DA-310 is used for sealing plastics or metals to other substrates, and as a raw material for adhesives. 收起 | |
| DA-500 | DCC (Dairen Chemical Corp.) | DA-500 is an aqueous, non-plasticized, milky white copolymer dispersion based on vinyl acetate and ethylene. After evaporation of its water content, DA-500 forms a flexible film with adhesive properties for a broad range of applications. DA-500 is used in...展开 DA-500 is an aqueous, non-plasticized, milky white copolymer dispersion based on vinyl acetate and ethylene. After evaporation of its water content, DA-500 forms a flexible film with adhesive properties for a broad range of applications. DA-500 is used in base for EPI wood glue systems, as a base emulsion for floor, wall or ceiling adhesives, and plastic (PVC) or metal foil bonding. 收起 | |
| DA-502 | DCC (Dairen Chemical Corp.) | DA-502 is an aqueous, non-plasticized, milky white copolymer dispersion based on vinyl acetate and ethylene. After evaporation of its water content, DA-502 forms a flexible film with adhesive properties for a broad range of applications. It has a viscosit...展开 DA-502 is an aqueous, non-plasticized, milky white copolymer dispersion based on vinyl acetate and ethylene. After evaporation of its water content, DA-502 forms a flexible film with adhesive properties for a broad range of applications. It has a viscosity at 25 °C of 3000-4000 mPa.s. DA-502 is used in base for EPI wood glue systems, as a base emulsion for floor, wall or ceiling adhesives, and plastic (PVC) or metal foil bonding. 收起 | |
| DA-511 | DCC (Dairen Chemical Corp.) | DA-511 is an aqueous, non-plasticized, milky white copolymer dispersion based on vinyl acetate and ethylene. After evaporation of its water content, DA-511 forms a flexible film with adhesive properties for a broad range of applications. It has a viscosit...展开 DA-511 is an aqueous, non-plasticized, milky white copolymer dispersion based on vinyl acetate and ethylene. After evaporation of its water content, DA-511 forms a flexible film with adhesive properties for a broad range of applications. It has a viscosity at 25 °C of 1500-2500 mPa.s. DA-511 is used in base for EPI wood glue systems, as a base emulsion for floor, wall or ceiling adhesives, and plastic (PVC) or metal foil bonding. 收起 | |
| DA-523 | DCC (Dairen Chemical Corp.) | DA-523 is an aqueous, non-plasticized, milky white copolymer dispersion based on vinyl acetate and ethylene. After evaporation of its water content, DA-523 forms a flexible film with adhesive properties for a broad range of applications. It has a viscosit...展开 DA-523 is an aqueous, non-plasticized, milky white copolymer dispersion based on vinyl acetate and ethylene. After evaporation of its water content, DA-523 forms a flexible film with adhesive properties for a broad range of applications. It has a viscosity at 25 °C of 700-1000 mPa.s. DA-523 is used in base for EPI wood glue systems, as a base emulsion for floor, wall or ceiling adhesives, and plastic (PVC) or metal foil bonding. 收起 | |
| DA-524 | DCC (Dairen Chemical Corp.) | DA-524 is an aqueous, non-plasticized, milky white copolymer dispersion based on vinyl acetate and ethylene. After evaporation of its water content, DA-524 forms a tough but still flexible film with adhesive properties for a broad range of applications. I...展开 DA-524 is an aqueous, non-plasticized, milky white copolymer dispersion based on vinyl acetate and ethylene. After evaporation of its water content, DA-524 forms a tough but still flexible film with adhesive properties for a broad range of applications. It has a viscosity at 25 °C of 1500-2500 mPa.s. DA-524 is used in base for EPI wood glue systems, as a base emulsion for floor, wall or ceiling adhesives, and plastic (PVC) or metal foil bonding. 收起 | |
| Decotherm™ 260 E | Lawter | Decotherm™ 260 E is a polyester resin dissolved in tripropylene glycol that has the benefit of high pigment wetting, gloss, flow and transfer on high speed presses. It also has good adhesion to metals which is why it is considered ideal for use in metal d...展开 Decotherm™ 260 E is a polyester resin dissolved in tripropylene glycol that has the benefit of high pigment wetting, gloss, flow and transfer on high speed presses. It also has good adhesion to metals which is why it is considered ideal for use in metal deco inks. Such inks use the spindle printing or dry offset system of printing on 2-piece cans. 收起 | |
| Decotherm™ 290 E | Lawter | Decotherm™ 290 E is a structured polyester resin that has low tack and misting properties, shows good transfer on high speed presses and displays adhesion to metals. It is used in metal deco inks using the spindle printing or dry offset method for 2-piece...展开 Decotherm™ 290 E is a structured polyester resin that has low tack and misting properties, shows good transfer on high speed presses and displays adhesion to metals. It is used in metal deco inks using the spindle printing or dry offset method for 2-piece cans. It shows good color retention and is also used in white and colored ink applications. 收起 | |
| Ultrapoly™ 210 A | Lawter | Ultrapoly™ 210 A is a sheet-fed polyethylene compound that is non-volatile and is a hard-drying and fast setting vehicle. It is recommended in situations that call for mar resistance, slip and abrasion. Ultrapoly™ 210 A protects the film during the earli...展开 Ultrapoly™ 210 A is a sheet-fed polyethylene compound that is non-volatile and is a hard-drying and fast setting vehicle. It is recommended in situations that call for mar resistance, slip and abrasion. Ultrapoly™ 210 A protects the film during the earliest phases of the printing process while developing toughness over time. It is ideally used in sheet-fed offset inks, in OPV, metal decorating and in UV inks. 收起 |