| Aluminum Silicate, Extender Slurries (Formulation #21-10006) | Patcham USA | Gradually add cellulosic thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1. Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing f...展开 Gradually add cellulosic thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1. Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing for 10 minutes at 2 ms-1. Grind the mill base using Glass beads for 2 hours at 21 ms-1 μm / gauge 7+ NS. 收起 | |
| Calcium Carbonate, Extender Slurries (Formulation #21-10006) | Patcham USA | Gradually add cellulosic thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1. Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing f...展开 Gradually add cellulosic thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1. Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing for 10 minutes at 2 ms-1. Grind the mill base using Glass beads for 2 hours at 21 ms-1 μm/ gauge 7+ NS. 收起 | |
| Dispersion-Silicate Facade Paint, Water Based (Formulation #F14402.0 [1]) | Hoffmann Mineral | 硅酸盐乳液外墙涂料，水性 (配方#F14402.0 [1]) ，含SILLITIN N 85 | |
| High Gloss White Coat Paint (Formulation #07-1021B) | Ashland | PVC20％ - Synaqua*4804 醇酸树脂乳液高光白色面漆，含有AquaFlow™NLS-205和AquaFlow™NMS-450流变改性剂。 | |
| High Gloss White Top Coat - Higher Solids (Formulation #07-1022B) | Ashland | PVC20％ - Uradil* AZ785-Z52 醇酸树脂乳液高光白色面漆，含有AquaFlow™NMS-450和AquaFlow™NHS-300流变改性剂。 | |
| High Gloss White Top Coat (Formulation #07-1023B) | Ashland | PVC19％ - Primal* HG74D 丙烯酸高光白色涂料，含有AquaFlow™NMS-450和AquaFlow™NHS-350流变改性剂。 | |
| High Gloss White Top Coat (Formulation #07-1024B) | Ashland | PVC19％ - Primal* HG74D - 丙烯酸高光白色涂料，含有AquaFlow™XLS-500和AquaFlow™NHS-300流变改性剂。 | |
| High Gloss White Top Coat (Formulation #07-1025B) | Ashland | PVC20％ - Uradil* AZ785-Z52 醇酸树脂乳液高光白色面漆，含有AquaFlow™XLS-530和AquaFlow™NMS-450流变改性剂。 | |
| High Gloss White Top Coat (Formulation #07-1030B) | Ashland | 这个配方可于高光泽涂料，高光泽白色。它含AquaFlow™NMS-450，AquaFlow™NHS-350，NUOSEPT®BIC和DEXTROL®OC180。 | |
| High Quality Facade Paint, Solvent-based (Formulation #F20102.0 [1]) | Hoffmann Mineral | 高品质外墙涂料，溶剂型（配方#F20102.0 [1]），含SILLITIN Z 89 | |
| Interior / Exterior Deeptone Semi Gloss Paint (Formulation #07-1018B) | Ashland | PVC43％ - Acronal* S-559 苯丙烯酸深色调半光泽涂料，含有AquaFlow™XLS-500和AquaFlow™NHS-300流变改性剂。 | |
| Interior / Exterior Semi Gloss Paint (Formulation #07-1031B) | Ashland | PVC30％ - NEOCRYL* XK-90 丙烯酸半光白色涂料，含有AquaFlow™XLS-500和AquaFlow™NHS-300流变改性剂。 | |
| Interior / Exterior Semi Matt Paint (Formulation #07-1034A) | Ashland | PVC38％ - Acronal* S559 苯乙烯丙烯酸内饰半哑光白漆，含有Natrosol™HE 3KB疏水改性的羟乙基纤维素（HMHEC）及AquaFlow™NMS-450流变改性剂。 | |
| Interior / Exterior Semi Matt Paint (Formulation #07-1035A) | Ashland | PVC38％ - Mowilith* LDM1871 醋酸乙烯酯乙烯内饰半哑光白漆，含有Natrosol™HE 3KB疏水改性的羟乙基纤维素（HMHEC）。 | |
| Interior / Exterior Semi-Gloss Paint (Formulation #07-1032B) | Ashland | PVC30％ - NEOCRYL* XK-90 丙烯酸半光白色涂料，含有AquaFlow™XLS-530和AquaFlow™NHS-350流变改性剂。 | |
| Interior / Exterior Semi-Matt Paint (Formulation #07-1033B) | Ashland | PVC38％ - Mowilith*LDM1871 醋酸乙烯酯乙烯内饰半亚光白漆，含有Natrosol Plus™330疏水改性的羟乙基纤维素（HMHEC）及AquaFlow™NMS-450流变改性剂。 | |
| Interior / Exterior Semi-Matt Paint (Formulation #07-1036B) | Ashland | PVC38％ - ALBERDINGK*AS6002 苯乙烯丙烯酸内饰半哑光白漆，含有Natrosol™Plus330疏水改性的羟乙基纤维素（HMHEC）。 | |
| Interior / Exterior Semi-Matt Paint (Formulation #07-1037B) | Ashland | PVC38％ -Vinnapas* EZ3010 醋酸乙烯酯乙烯内饰半哑光白漆，含有Natrosol™Plus 330疏水改性的羟乙基纤维素（HMHEC）。 | |
| Interior/Exterior Gloss Acrylic Dry TiO2 | Ashland | ||
| Interior/Exterior Gloss Paint (Formulation #21-10005) | Patcham USA | Gradually add Cellulosic Thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing ...展开 Gradually add Cellulosic Thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing for 10 minutes at 2 ms-1. Grind at 4 ms-1 until desired Hegman gauge is achieved- 7+ NS/ <10 μm. 收起 | |
| Interior/Exterior Matt Paint (Formulation #21-10005) | Patcham USA | Gradually add Cellulosic Thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing ...展开 Gradually add Cellulosic Thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing for 10 minutes at 2 ms-1. Grind at 4 ms-1 until desired Hegman gauge is achieved. 5+ NS/ min. of 20 μm. 收起 | |
| Interior/Exterior Semi Glossy Paint Waterborne Coatings (Formulation #21-10005) | Patcham USA | Gradually add Cellulosic Thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing ...展开 Gradually add Cellulosic Thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing for 10 minutes at 2 ms-1. Grind at 4 ms-1 until desired Hegman gauge is achieved. -7 NS/ min. of 15 μm. 收起 | |
| Interior/Exterior Semi-Matt Paint (Formulation #07-1039B) | Ashland | PVC 38% - Acronal S559* styrene acrylic semi-matt white paint. | |
| Matt Paint 1 (Formulation #SPF_CTG_021_2203) | Arkema Rheology & Specialty Additives | This matt paint features Ecodis™ P 50. | |
| Matt Paint 2 (Formulation #SPF_CTG_022_2203) | Arkema Rheology & Specialty Additives | This matt paint features Ecodis™ P 50. | |
| Matt Paint 3 (Formulation #SPF_CTG_023_2203) | Arkema Rheology & Specialty Additives | This matt paint features Ecodis™ P 50. | |
| Talc, Extender Slurries (Formulation #21-10006) | Patcham USA | Gradually add cellulosic thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing ...展开 Gradually add cellulosic thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing 10 minutes at 2 ms-1. Grind the mill base using Glass beads for 2 hours at 21 ms-1 μm / gauge 7+ NS. 收起 | |
| Zinc Oxide, Extender Slurries (Formulation #21-10006) | Patcham USA | Gradually add cellulosic thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing ...展开 Gradually add cellulosic thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing 10 minutes at 2 ms-1. Grind the mill base using Glass beads for 2 hours at 21 ms-1 μm / gauge 7+ NS. 收起 |