| 2K Waterborne Wall Paint - White (Formulation #142/148-024 - 022) | Incorez Ltd. | This white waterborne wall paint features Amirez 142 and Amirez 148/024. | |
| ACRONAL® PLUS 4415 Stain Blocking Primer | BASF Dispersions & Resins | Acronal PLUS 4415 is a styrene-acrylic latex for interior and exterior stain blocking primers at 50 g/L VOC. The latex can be widely applied, offering consistent, high-quality results for both interior and exterior primers. Acronal PLUS 4415 demonstrates ...展开 Acronal PLUS 4415 is a styrene-acrylic latex for interior and exterior stain blocking primers at 50 g/L VOC. The latex can be widely applied, offering consistent, high-quality results for both interior and exterior primers. Acronal PLUS 4415 demonstrates limited ropes and flakes during sanding and excellent interior stain control. This latex further outperforms commercial products in both adhesion and alkali resistance. Acronal PLUS 4415 is the solution for the premium stain blocking primer market. 收起 | |
| Aluminum Silicate, Extender Slurries (Formulation #21-10006) | Patcham USA | Gradually add cellulosic thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1. Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing f...展开 Gradually add cellulosic thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1. Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing for 10 minutes at 2 ms-1. Grind the mill base using Glass beads for 2 hours at 21 ms-1 μm / gauge 7+ NS. 收起 | |
| Calcium Carbonate, Extender Slurries (Formulation #21-10006) | Patcham USA | Gradually add cellulosic thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1. Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing f...展开 Gradually add cellulosic thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1. Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing for 10 minutes at 2 ms-1. Grind the mill base using Glass beads for 2 hours at 21 ms-1 μm/ gauge 7+ NS. 收起 | |
| Ceiling Paint (Formulation #051414) | Vanderbilt Minerals, LLC | A ceiling paint which utilizes the products DARVAN® 7-N Dispersant, PYRAX® ABB Pyrophyllite, and VANSIL® W-20 Wollastonite. | |
| Fire Resistant Coating | Buckman Laboratories, Inc. | This formula for fire resistant coating utilizes the product Bulab® Flamebloc. | |
| Fire-Resistant Interior Flat Wall Paint | Buckman Laboratories, Inc. | This formula for fire resistant interior flat wall paint utilizes the product Bulab® Flamebloc. | |
| Fire-Resistant Semigloss Enamel | Buckman Laboratories, Inc. | This formula for fire resistant semigloss enamel utilizes the product Bulab® Flamebloc. | |
| Flat Tintable Paint Formulation | Buckman Laboratories, Inc. | This is a formula for a flat tintable paint utilizing the products Bubreak® 448 and Busperse® 39. | |
| General Purpose Latex Primer | Buckman Laboratories, Inc. | This is a formula for a general purpose latex primer utilizing the product Busan® 11-M1. | |
| Interior Dispersion Paint (Formulation #F10102.2 [15]) | Hoffmann Mineral | 户内乳胶漆 (配方#F10102.2 [15])，含SILLITIN Z 89 | |
| Interior Flat Vinyl Acrylic Dry TiO2 | Ashland | ||
| Interior Latex Egg Shell Paint (Formulation #041111) | Vanderbilt Minerals, LLC | A formulation for an interior latex egg shell paint using VANSIL® W-30 and DARVAN® 7-N. | |
| Interior Latex Semi-Gloss Paint (Formulation #021711) | Vanderbilt Minerals, LLC | A formulation for an interior latex semi-gloss paint. | |
| Interior Semi-Gloss Paint (Formulation #062512) | Vanderbilt Minerals, LLC | An interior semi-gloss paint formulation using DARVAN® 7-N, VANSIL® W-30 and VAN GEL® O. | |
| Interior Semi-Gloss Wall Paint (Formulation #082012) | Vanderbilt Minerals, LLC | A formulation for an interior semi-gloss wall paint. | |
| Interior Semi-Gloss Wall Paint (Formulation #082112) | Vanderbilt Minerals, LLC | An interior semi-gloss wall paint formulation using DARVAN® 561 and VANSIL® W-30. | |
| Interior Stain Blocking Primer (Formulation #4641-007) | BASF Dispersions & Resins | This interior stain blocking primer features Acronal PLUS® 4641. | |
| Interior/Exterior Gloss Paint (Formulation #21-10005) | Patcham USA | Gradually add Cellulosic Thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing ...展开 Gradually add Cellulosic Thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing for 10 minutes at 2 ms-1. Grind at 4 ms-1 until desired Hegman gauge is achieved- 7+ NS/ <10 μm. 收起 | |
| Interior/Exterior Matt Paint (Formulation #21-10005) | Patcham USA | Gradually add Cellulosic Thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing ...展开 Gradually add Cellulosic Thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing for 10 minutes at 2 ms-1. Grind at 4 ms-1 until desired Hegman gauge is achieved. 5+ NS/ min. of 20 μm. 收起 | |
| Interior/Exterior Semi Glossy Paint Waterborne Coatings (Formulation #21-10005) | Patcham USA | Gradually add Cellulosic Thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing ...展开 Gradually add Cellulosic Thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing for 10 minutes at 2 ms-1. Grind at 4 ms-1 until desired Hegman gauge is achieved. -7 NS/ min. of 15 μm. 收起 | |
| Low VOC Interior Flat Latex Wall Paint with Good Scrub Resistance (Formulation #062414) | Vanderbilt Minerals, LLC | A formulation for a low-VOC interior flat latex wall paint. This scrub-resistant formula features the products VANSIL® CK-20 Wollastonite and DARVAN® 7-N Dispersant. | |
| Reducing Leachable Components in Waterborne Architectural Paints | BASF Dispersions & Resins | The composition of waterborne paints and coatings rely on several surface active or water soluble components for their production, stability and performance. Unfortunately these ingredients can migrate to the paint surface leaving visible streaks referred...展开 The composition of waterborne paints and coatings rely on several surface active or water soluble components for their production, stability and performance. Unfortunately these ingredients can migrate to the paint surface leaving visible streaks referred to as “Surfactant Leaching/Staining” or “Snail Trails”. Staining typically occurs after the paint has been exposed to specific conditions such as high humidity and water condensation. The presence of water on a paint surface can concentrate leachable materials into a non-uniform pattern of visible glossy streaks. A careful selection of formulation ingredients can help reduce the extent of staining. 收起 | |
| Talc, Extender Slurries (Formulation #21-10006) | Patcham USA | Gradually add cellulosic thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing ...展开 Gradually add cellulosic thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing 10 minutes at 2 ms-1. Grind the mill base using Glass beads for 2 hours at 21 ms-1 μm / gauge 7+ NS. 收起 | |
| Tannin Stain Blocking Primer (Formulation #4410-001) | BASF Dispersions & Resins | This tannin stain blocking primer features Acronal® 4410. | |
| Universal Stain-Blocking Primer - White (Formulation #EPS 2843 WHT1) | EPS Materials | Universal Stain-Blocking Primer - White (Formulation #EPS 2843 WHT1) formulation information. | |
| White Gloss using Incorez 142 & Incorez 148/024 | Incorez Ltd. | 这是一款使用了Incorez 142和Incorez 148/024产品的白色光泽墙面漆。 | |
| White Semi-Gloss Formulation | Buckman Laboratories, Inc. | This is a formula for white semi-gloss utilizing the products Bubreak® 448 and Busperse® 39. | |
| White Shingle Stain | Buckman Laboratories, Inc. | This formula for white shingle stain utilizes the product Bulab® Flamebloc. | |
| Zero VOC High Quality Interior Flat Wall Paint (Formulation #071808) | Vanderbilt Minerals, LLC | A formulation for a zero VOC high quality interior flat wall paint using VANSIL® W-40. | |
| Zinc Oxide, Extender Slurries (Formulation #21-10006) | Patcham USA | Gradually add cellulosic thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing ...展开 Gradually add cellulosic thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing 10 minutes at 2 ms-1. Grind the mill base using Glass beads for 2 hours at 21 ms-1 μm / gauge 7+ NS. 收起 |